Stanyl? TW363
聚酰胺 46
產(chǎn)品說明:
Heat Stabilized, Impact Modified
Special Features:
Used In:
Stanyl? is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
添加劑 | |
特性 | |
用途 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | |
樹脂ID (ISO 1043) | |
密度 | 1.10 | -- | g/cm3 | ISO 1183 |
收縮率 |
|
|
| ISO 294-4 |
橫向流量 | 2.0 | -- | % |
|
流量 | 2.0 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
飽和, 73°F | 11 | -- | % |
|
平衡, 73°F, 50% RH | 3.0 | -- | % |
|
拉伸模量 |
|
|
| ISO 527-2 |
-- | 268000 | 87000 | psi |
|
248°F | 58000 | -- | psi |
|
320°F | 50800 | -- | psi |
|
拉伸應(yīng)力 |
|
|
| ISO 527-2 |
屈服 | 8700 | 6530 | psi |
|
屈服, 248°F | 5080 | -- | psi |
|
屈服, 320°F | 4350 | -- | psi |
|
拉伸應(yīng)變 (屈服) | 20 | 25 | % | ISO 527-2 |
標(biāo)稱拉伸斷裂應(yīng)變 | > 50 | > 50 | % | ISO 527-2 |
彎曲模量 |
|
|
| ISO 178 |
-- | 261000 | 79800 | psi |
|
248°F | 58000 | -- | psi |
|
320°F | 50800 | -- | psi |
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eA |
-22°F | 12 | 14 | ft·lb/in2 |
|
73°F | 36 | 59 | ft·lb/in2 |
|
簡(jiǎn)支梁無缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eU |
-22°F | 無斷裂 | 無斷裂 |
|
|
73°F | 無斷裂 | 無斷裂 |
|
|
懸壁梁缺口沖擊強(qiáng)度 |
|
|
| ISO 180/1A |
-40°F | 19 | 19 | ft·lb/in2 |
|
73°F | 38 | 59 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 392 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 194 | -- | °F | ISO 75-2/A |
玻璃轉(zhuǎn)化溫度 2 | 167 | -- | °F | ISO 11357-2 |
維卡軟化溫度 | 482 | -- | °F | ISO 306/B50 |
熔融溫度 2 | 563 | -- | °F | ISO 11357-3 |
線形熱膨脹系數(shù) |
|
|
| ISO 11359-2 |
流動(dòng) | 8.9E-5 | -- | in/in/°F |
|
橫向 | 1.0E-4 | -- | in/in/°F |
|
Effective Thermal Diffusivity | 9.82E-7 | -- | m2/s |
|
Thermal Index - 5000 hr | 275 | -- | °F | IEC 60216 |
體積電阻率 | 1.0E+15 | 1.0E+9 | ohms·cm | IEC 60093 |
介電強(qiáng)度 | 640 | 380 | V/mil | IEC 60243-1 |
相對(duì)電容率 |
|
|
| IEC 60250 |
100 Hz | 3.60 | 14.0 |
|
|
1 MHz | 3.20 | 4.00 |
|
|
耗散因數(shù) |
|
|
| IEC 60250 |
100 Hz | 0.012 | 0.65 |
|
|
1 MHz | 0.019 | 0.10 |
|
|
漏電起痕指數(shù) | 475 | -- | V | IEC 60112 |
極限氧指數(shù) | 27 | -- | % | ISO 4589-2 |
熔體密度 | 0.913 | -- | g/cm3 |
|
熔體導(dǎo)熱性 | 1.7 | -- | Btu·in/hr/ft2/°F |
|
Specific Heat Capacity of Melt | 0.609 | -- | Btu/lb/°F |
|
干燥溫度 | 176 | °F |
干燥時(shí)間 | 4.0 到 8.0 | hr |
料筒后部溫度 | 536 到 608 | °F |
料筒中部溫度 | 572 到 608 | °F |
料筒前部溫度 | 572 到 608 | °F |
射嘴溫度 | 572 到 608 | °F |
加工（熔體）溫度 | 590 到 608 | °F |
模具溫度 | 176 到 248 | °F |
注射速度 | 中等偏快 |
|
背壓 | 290 到 1450 | psi |
|
|
|
如需恩驊力（Envalior）原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我司工作人員，謝謝！